| Wrought copper alloy C70600 (Copper-Nickel 10%) | ||||
| Chemical composition: Ni=10%, Fe=1.4%, Cu=balance | ||||
| Value in US unit | Value in metric unit | Property | ||
| Property | Value in metric unit | Value in US unit | ||
| Density | 8.94 *10³ | kg/m³ | 558 | lb/ft³ |
|---|---|---|---|---|
| Modulus of elasticity | 124 | GPa | 18000 | ksi |
| Thermal expansion (20 ºC) | 17.1*10-6 | ºCˉ¹ | 9.5*10-6 | in/(in* ºF) |
| Specific heat capacity | 377 | J/(kg*K) | 0.090 | BTU/(lb*ºF) |
| Thermal conductivity | 45.0 | W/(m*K) | 312 | BTU*in/(hr*ft²*ºF) |
| Electric resistivity | 19.1*10-8 | Ohm*m | 19.1*10-6 | Ohm*cm |
| Tensile strength (annealed) | 303 | MPa | 44000 | psi |
| Yield strength (annealed) | 110 | MPa | 16000 | psi |
| Elongation (annealed) | 42 | % | 42 | % |
| Hardness (annealed) | 15 | RB | 15 | RB |
| Tensile strength (cold work) | 414 | MPa | 60000 | psi |
| Yield strength (cold work) | 393 | MPa | 57000 | psi |
| Elongation (cold work) | 10 | % | 10 | % |
| Hardness (cold work) | 72 | RB | 72 | RB |
| Annealing temperature | 600-850 | ºC | 1100-1500 | ºF |
| Liquidus temperature | 1149 | ºC | 2100 | ºF |
| Solidus temperature | 1099 | ºC | 2010 | ºF |