Wrought copper alloy C75400 (Nickel Silver 65-15)

(submitted by the website administration)

Wrought copper alloy C75400 (Nickel Silver 65-15)
Chemical composition: Ni=15%, Zn=20%, Cu=65%
Property Value in metric unit Value in US unit
Density 8.69*10³ kg/m³ 542 lb/ft³
Modulus of elasticity 124 GPa 18000 ksi
Thermal expansion (20 ºC) 16.2*10-6 ºCˉ¹ 9.0*10-6 in/(in* ºF)
Specific heat capacity 377 J/(kg*K) 0.090 BTU/(lb*ºF)
Thermal conductivity 36.3 W/(m*K) 252 BTU*in/(hr*ft²*ºF)
Electric resistivity 24.6*10-8 Ohm*m 24.6*10-6 Ohm*cm
Tensile strength (annealed) 365 MPa 53000 psi
Yield strength (annealed) 124 MPa 18000 psi
Elongation (annealed) 43 % 43 %
Hardness (annealed) 27 R30T 27 R30T
Tensile strength (cold work) 634 MPa 92000 psi
Yield strength (cold work) 545 MPa 79000 psi
Elongation (cold work) 2 % 2 %
Shear strength (cold work) 372 MPa 54000 psi
Hardness (cold work) 77 R30T 77 R30T
Annealing temperature 600-850 ºC 1100-1500 ºF
Liquidus temperature 1077 ºC 1970 ºF
Solidus temperature 1038 ºC 1900 ºF