Wrought aluminum-manganese alloy 3003

(submitted by the website administration)

Wrought aluminum-manganese alloy 3003
Chemical composition: Cu=0.12%, Mn=1.25%, Al balance
Property Value in metric unit Value in US unit
Density 2.73 *10³ kg/m³ 170 lb/ft³
Modulus of elasticity 69 GPa 10000 ksi
Thermal expansion (20 ºC) 23.2*10-6 ºCˉ¹ 12.9*10-6 in/(in* ºF)
Specific heat capacity 893 J/(kg*K) 0.213 BTU/(lb*ºF)
Thermal conductivity 193 W/(m*K) 1340 BTU*in/(hr*ft²*ºF)
Electric resistivity 3.49*10-8 Ohm*m 3.49*10-6 Ohm*cm
Tensile strength (annealed) 110 MPa 16000 psi
Yield strength (annealed) 41 MPa 6000 psi
Elongation (annealed) 30 % 30 %
Shear strength (annealed) 76 MPa 11000 psi
Fatigue strength (annealed) 48 MPa 7000 psi
Hardness (annealed) 28 HB 28 HB
Tensile strength (H18) 200 MPa 29000 psi
Yield strength (H18) 186 MPa 27000 psi
Elongation (H18) 4 % 4 %
Shear strength (H18) 124 MPa 18000 psi
Fatigue strength (H18) 69 MPa 10000 psi
Hardness (H18) 55 HB 55 HB
Hardness (H12) 35 HB 35 HB
Hardness (H14) 40 HB 40 HB
Hardness (H16) 47 HB 47 HB
Annealing temperature 413 ºC 775 ºF