to Wrought aluminum-magnesium alloys (5xxx)
to Properties of aluminum alloys
(submitted by the website administration)
| Wrought aluminum-magnesium alloy 5005 | ||||
| Chemical composition: Mg=0.80%, Al balance | ||||
| Property | Value in metric unit | Value in US unit | ||
| Density | 2.70 *10³ | kg/m³ | 169 | lb/ft³ |
|---|---|---|---|---|
| Modulus of elasticity | 69 | GPa | 10000 | ksi |
| Thermal expansion (20 ºC) | 23.8*10-6 | ºCˉ¹ | 13.2*10-6 | in/(in* ºF) |
| Specific heat capacity | 900 | J/(kg*K) | 0.215 | BTU/(lb*ºF) |
| Thermal conductivity | 200 | W/(m*K) | 1390 | BTU*in/(hr*ft²*ºF) |
| Electric resistivity | 3.32*10-8 | Ohm*m | 3.32*10-6 | Ohm*cm |
| Tensile strength (annealed) | 124 | MPa | 18000 | psi |
| Yield strength (annealed) | 41 | MPa | 6000 | psi |
| Elongation (annealed) | 25 | % | 25 | % |
| Shear strength (annealed) | 76 | MPa | 11000 | psi |
| Hardness (annealed) | 28 | HB | 28 | HB |
| Tensile strength (H38) | 200 | MPa | 29000 | psi |
| Yield strength (H38) | 186 | MPa | 27000 | psi |
| Elongation (H38) | 5 | % | 5 | % |
| Shear strength (H38) | 110 | MPa | 16000 | psi |
| Hardness (H38) | 51 | HB | 51 | HB |
| Annealing temperature | 343 | ºC | 650 | ºF |