| Cast copper alloy C92200 (Naval M Bronze) | ||||
| Chemical composition: Sn=6.0%, Pb=1.5%, Zn=4.5%, Cu=88% | ||||
| Property | Value in metric unit | Value in US unit | ||
| Density | 8.64 *10³ | kg/m³ | 539 | lb/ft³ |
|---|---|---|---|---|
| Modulus of elasticity | 96.5 | GPa | 14000 | ksi |
| Thermal expansion (20 ºC) | 18.0*10-6 | ºCˉ¹ | 10.0*10-6 | in/(in* ºF) |
| Specific heat capacity | 377 | J/(kg*K) | 0.090 | BTU/(lb*ºF) |
| Thermal conductivity | 69.6 | W/(m*K) | 482 | BTU*in/(hr*ft²*ºF) |
| Electric resistivity | 12.0*10-8 | Ohm*m | 12.0*10-6 | Ohm*cm |
| Tensile strength (sand cast) | 276 | MPa | 40000 | psi |
| Yield strength (sand cast) | 138 | MPa | 20000 | psi |
| Elongation (sand cast) | 30 | % | 30 | % |
| Fatigue strength (sand cast) | 76 | MPa | 11000 | psi |
| Hardness (sand cast) | 65 | HB(500) | 65 | HB(500) |
| Liquidus temperature | 988 | ºC | 1810 | ºF |
| Solidus temperature | 826 | ºC | 1518 | ºF |