Cast aluminum alloy 852.0

(submitted by the website administration)

Cast aluminum alloy 852.0
Chemical composition: Cu=2%, Mg=0.75%, Ni=1.2%, Sn=6.25%, Al balance, die casting
Property	Value in metric unit		Value in US unit
Density	2.88 *10³	kg/m³	180	lb/ft³
Modulus of elasticity	71	GPa	10300	ksi
Thermal expansion (20 ºC)	23.2*10^-6	ºCˉ¹	12.9*10^-6	in/(in* ºF)
Specific heat capacity	963	J/(kg*K)	0.230	BTU/(lb*ºF)
Thermal conductivity	172	W/(m*K)	1190	BTUin/(hrft²*ºF)
Electric resistivity	3.8*10^-8	Ohm*m	3.8*10^-6	Ohm*cm
Heat of fusion	3.89*10⁵	J/kg	167	BTU/lb
Liquidus temperature	635	ºC	1175	ºF
Solidus temperature	204	ºC	400	ºF
Tensile strength (F), min	186	MPa	27000	psi
Elongation (F), min	3	%	3	%
Shear strength (F)	115	MPa	16700	psi
Hardness (F) , range	55-85	HB	55-85	HB