Cast aluminum alloy 713.0

(submitted by the website administration)

Cast aluminum alloy 713.0
Chemical composition: Cu=0.7%, Mg=0.35%, Zn=7.5%, Al balance, sand casting
Property	Value in metric unit		Value in US unit
Density	2.81 *10³	kg/m³	175	lb/ft³
Modulus of elasticity	71	GPa	10300	ksi
Thermal expansion (20 ºC)	24.1*10^-6	ºCˉ¹	13.4*10^-6	in/(in* ºF)
Specific heat capacity	963	J/(kg*K)	0.230	BTU/(lb*ºF)
Thermal conductivity	121	W/(m*K)	841	BTUin/(hrft²*ºF)
Electric resistivity	5.7*10^-8	Ohm*m	5.7*10^-6	Ohm*cm
Heat of fusion	3.89*10⁵	J/kg	167	BTU/lb
Liquidus temperature	638	ºC	1180	ºF
Solidus temperature	593	ºC	1100	ºF
Tensile strength (F) ,min.	221	MPa	32000	psi
Yield strength (F) ,min.	152	MPa	22000	psi
Elongation (F) ,min.	3	%	3	%
Shear strength (F)	180	MPa	26100	psi
Fatigue strength (F)	60	MPa	8700	psi
Hardness (F) , range	60-90	HB	60-90	HB
Tensile strength (T5)	235	MPa	34100	psi
Yield strength (T5)	175	MPa	25400	psi
Elongation (T5)	4	%	4	%