Cast aluminum alloy 333.0

(submitted by the website administration)

Cast aluminum alloy 333.0
Chemical composition: Si=9.0%, Cu=3.5%, Mg=0.28%, Al balance, permanent mold casting
Property	Value in metric unit		Value in US unit
Density	2.77 *10³	kg/m³	173	lb/ft³
Modulus of elasticity	73	GPa	10600	ksi
Thermal expansion (20 ºC)	20.5*10^-6	ºCˉ¹	11.4*10^-6	in/(in* ºF)
Specific heat capacity	963	J/(kg*K)	0.230	BTU/(lb*ºF)
Thermal conductivity	105	W/(m*K)	725	BTUin/(hrft²*ºF)
Electric resistivity	6.6*10^-8	Ohm*m	6.6*10^-6	Ohm*cm
Heat of fusion	3.89*10⁵	J/kg	167	BTU/lb
Liquidus temperature	585	ºC	1085	ºF
Solidus temperature	516	ºC	960	ºF
Tensile strength (F), min.	193	MPa	28000	psi
Shear strength (F)	119	MPa	17300	psi
Hardness (F) , range	65-100	HB	65-100	HB
Tensile strength (T6), min	241	MPa	35000	psi
Shear strength (T6)	147	MPa	21300	psi
Hardness (T6) , range	85-115	HB	85-115	HB