| Cast aluminum alloy 443.0 | ||||
| Chemical composition: Si=5.3%, Al balance, permanent mold casting | ||||
| Property | Value in metric unit | Value in US unit | ||
| Density | 2.69 *10³ | kg/m³ | 168 | lb/ft³ |
|---|---|---|---|---|
| Modulus of elasticity | 71 | GPa | 10300 | ksi |
| Thermal expansion (20 ºC) | 22.1*10-6 | ºCˉ¹ | 12.3*10-6 | in/(in* ºF) |
| Specific heat capacity | 963 | J/(kg*K) | 0.230 | BTU/(lb*ºF) |
| Thermal conductivity | 146 | W/(m*K) | 1010 | BTU*in/(hr*ft²*ºF) |
| Electric resistivity | 4.6*10-8 | Ohm*m | 4.6*10-6 | Ohm*cm |
| Heat of fusion | 3.89*105 | J/kg | 167 | BTU/lb |
| Liquidus temperature | 632 | ºC | 1170 | ºF |
| Solidus temperature | 574 | ºC | 1065 | ºF |
| Tensile strength (F) | 160 | MPa | 23200 | psi |
| Yield strength (F) | 70 | MPa | 10150 | psi |
| Elongation (F) | 6 | % | 6 | % |
| Shear strength (F) | 91 | MPa | 13200 | psi |
| Hardness (F) , range | 30-60 | HB | 30-60 | HB |
http://www.tntech.edu/me/courses/Zhang/ME30103110/Chap11pt4.ppt
http://www.ccm.udel.edu/Personnel/homepage/class_web/Lecture%20Notes/2004/AskelandPhuleNotes-
CH13Printable.ppt
http://www.aluminum.org/
http://www.aluminium.org/
http://www.cmse.ed.ac.uk/MSE3/Topics/MSE3-nonferrous.pdf
http://www.ndt-ed.org/GeneralResources/MaterialProperties/ET/et_matlprop_index.htm